Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Scientific Reports volume  13, Article number: 5063 (2023 ) Cite this article Methyl Hydroxyethyl Cellulosemhec

Effect of adding nano-materials on the properties of hydroxypropyl methylcellulose (HPMC) edible films | Scientific Reports

The bio-composite films based on Hydroxypropyl methylcellulose (HPMC) reinforced with silver nanoparticles (AgNPs) and Titanium oxide nanoparticles (TiO2-NPs) were developed. Some physical and mechanical properties: Tensile strength (TS), elongation (E), Young’s elastic modulus (EM), water vapor permeability (WVP) and transparency were determined. Antibacterial properties of these films were also studied. The tensile strength values of HPMC film reinforced with Ag NPs and TiO2-NPs and HPMC without nanoparticles were 39.24, 143.87 and 157.92 MPa, respectively. Elongation of the HMPC film was less than the HPMC film reinforced with AgNPs and TiO2-NPs, the results were 2, 35 and 42%, respectively. Additionally, Young’s elastic modulus of HMPC film was determined to be 19.62 MPa and the HPMC film reinforced with AgNPs and TiO2-NPs were 4.11 and 3.76 MPa, respectively. The values of WVP of HMPC film was higher than the HMPC film reinforced with AgNPs and TiO2-NPs, where they were 0.5076 × 10−3, 0.4596 × 10−3 and 0.4504 × 10−3 (g/msPa), respectively. Nano-composite films demonstrated strong antibacterial activity against tested pathogen bacteria in the contact surface zone. The antibacterial activites of AgNPs (~ 10 nm) at 80 ppm were more active than 20 and 40 ppm against foodborne pathogen i.e. Bacillus cereus and Escherichia coli, the inhibition zone diameters were 9 and 10 mm, respectively. As well, TiO2-NPs (~ 50 nm) at 80 ppm were more active than 20 and 40 ppm against B. cereus and Salmonella Typhimurium, the inhibition zone diameters were11 and 10 mm, respectively.

Shancong Huang, Xiyun Wang, … Xinxing Xia

Yijun Yao, Hongru Wang, … Yong Chai

Weronika Janik, Michał Nowotarski, ... Gabriela Dudek

In food sector, using nano-materials became very important and attractive, specially packing materials. Edible films and coating materials are commonly used as appropriate package materials to prolong the shelf-life of fresh food. These nanomaterials have distinguished properties compared to other materials due to their high surface area to volume ratio and other unique physiochemical properties such as color, solubility, strength, diffusivity, toxicity, magnetic, optical, and thermodynamic, etc.1. Nanotechnology has brought new industrial revolution and both developed and developing countries are interested in investing more in this technology2. Therefore, nanotechnology offers a wide range of opportunities for the development and application of structures, materials, or system with new properties in various areas like agriculture, food, and medicine, etc. The marketing of nanofood was estimated about US $35.5 billion in 2013 and US $100 billion in 20203.

Cellulose is the most abundant organic compound in the environment, which is renewable, recyclable, and biodegradable (into carbon, hydrogen, and oxygen)4. Notably, cellulose is more suitable for packing purpose as it is not a thermoplastic polymer, whereas its ester derivatives (methylcellulose (MC), hydroxypropyl methylcellulose (HPMC), hydroxypropyl cellulose (HPC), and ethyl cellulose (EC)) are biodegradable thermoplastic polymers. Hydroxypropyl methylcellulose and MC are soluble in the cold water, but after heating they form a thermally reversible and relatively hard gel by heating process at 50–80 °C5,6. Hydroxypropyl methylcellulose is odorless, flavorless, transparent, stable, oil‐resistant, nontoxic, and edible material with good film‐forming properties. It is a nonionic polymer with a linear structure of glucose molecules, in which its matrix is stabilized using hydrogen bonds7,8.

Silver nanoparticles are among the most explored nanoparticles, owing to their established antimicrobial potential against multiple commensals and pathogenic strains9. Besides bacterial strains, silver nanoparticles are known to be inhibitory against multiple fungi and also several viruses10. Silver targets bacterial metabolism by binding to its DNA, proteins and enzymes; resulting into bacteriostatic effects11. Silver nanoparticles destabilize and disrupt both the outer and cytoplasmic membranes12. Silver nanoparticles also inhibit the respiratory chain enzymes and can also stimulate the production of reactive oxygen species (ROS)13.

Naturally, titanium dioxide exists in three primary phases i.e., anatase, rutile, and brookite; having varied crystal sizes (diameter ranged from 2 to 6 nm)14. TiO2 possess photocatalytic abilities and at nanoscale TiO2 shows surface reactivity, which connects it with biological molecules (phosphorylated proteins and peptides) and DNA15. The surface energy of TiO2 nanoparticles amplifies with size the antibacterial properties of TiO2 is well known16 however, the antibacterial capacity of nano-TiO2 particles confined to the exposure of UV irradiation17. Although, the exact mechanism of biocidal activity of TiO2 is unclear, it may be attributed to its initial oxidative attack over the outer/inner bacterial cell membrane, alterations of TiO2 is unclear, it may be attributed to its initial oxidative attack over the outer/inner bacterial cell membrane, alterations of Coenzyme A-dependent enzyme activity, and DNA damage through hydroxyl radicals18.

Tensile strength (TS), water vapor permeability (WVP), % elongation (E), adsorption capacity and % soluble matter (SM) of water were studied in hydroxypropyl methylcellulose (HPMC) films reinforced by polyethylene glycol (PEG). The TS between 17 and 44 N/mm2 and the WVP of films was determined to be 0.232·1010–1.160·1010 g/msPa and %E between 14 and 97%, depending on composition. Moisture content (MC), ethanol content and pressure of PEG affected the film formation. Adding PEGs to the polymer matrix increased the WVP, elongation (E) and solubility but decreased the tensile strength (TS)19.

Food safety is an important concept and health concern in developed and developing countries20. The Center for Disease Control and Prevention Center21 reported that about 179 million people get sick, 428,000 hospitalized, 6000 deaths, and costed US $15.6 billion every year in USA from five food-borne pathogens. In addition, the World Bank report22 the food-borne illness in developing countries costed ~ US $110 billion, 600 million illness cases, and 420,000 premature deaths in Asia and Africa. Five-food-borne pathogens record about (88%) of the listed food concerned deaths: Salmonella nontyphoidal (35%), Norovirus (26%), Campylobacter (15%), Toxoplasma gondii (8%), and Escherichia coli (4%)21. One way to control food-borne pathogens and food spoilage is to develop antimicrobial films for packaging food.

Studying the properties of these film is very important for food preservation, therefor, the main aim of this work is to develop an edible film that made from hydroxypropyl methylcellulose (HPMC) reinforced with nanoparticles (AgNPs and TiO2NPs) and study some mechanical and antibacterial properties of these films. These properties include: tensile strength (TS), elongation (E), Young`s elastic modulus (EM), water vapor permeability (WVP) and transparency.

Silver nanoparticles (AgNPs), Titanium oxide nanoparticles (TiO2-NPs) and glycerol were purchased from Nano Gate Company, Cairo, Egypt. Hydroxypropyl methyl cellulose (HPMC) was supplied from G.I.D.C industrial Estate, India. Bacillus cereus (ATCC7464), Salmonella Typhimurium (ATCC14028), E. coli (ATCC87939), and Staphylococcus aureus (ATCC 6538) were obtained from (Microbiological Resources Center, MIRCEN, and Cairo, Egypt). As shown in Table 1, the compounds of bio-composite films were made from Distilled water, HMPC, glycerol, AgNPs and TiO2NPs.

Silver nanoparticles (AgNPs) have been prepared by chemical reduction method as reported by Pal et al23. For the synthesis of Ag nanoparticles SHARP make microwave oven (model: R259) was used. In a typical procedure, 10 ml of 1% (w/v) ethanolic solution of polyvinyl pyrrolidone (PVP) and 0.2 ml of 0.1 M AgNO3 were taken in a 25 ml closed conical flask and placed in a microwave oven that was operated at the 100% power of 800 W and frequency 2450 MHz for 5 s. The colorless solution instantaneously turned to the characteristic pale yellow colour, indicating the formation of silver nanoparticles. The advantage of microwave-mediated synthesis over the conventional heating is the improved kinetics of the reaction generally by one or two order of magnitude, due to rapid initial heating and the generation of localized high-temperature zones at reaction sites24.

Titanium oxide nanoparticles (TiO2-NPs) were prepared according to Salah et al25 with some modification. Briefly, the metallic compounds size (~ 0.6 ± 1 μm, 120 purity 99.9%, Loba, Chemi, Pvt. Ltd, India) was milled in steel cells (250 mL) using hardened steel balls (diameter 15 mm, weight 32 g) in ambient atmosphere for different times ranging from 2 to 50 h. The mechanical milling was performed in a horizontal oscillatory mill (Retsch, PM 400) operating at 25 Hz. The mixture ratio of steel balls and powders was around 15:1 by weight percent. Two parallel cells were used in this experiment (the total weight for the sample powder was 20 g).

Hydroxy propyl methyl cellulose (HPMC) was prepared according to De Moura et al26 with some modification. Briefly, each 40 g HPMC was dissolved in 1000 mL distilled water at 70 °C and stirred at 1000 rpm/min for 2 h to a complete dissolving. A 1 mL of glycerol 30% was add as plasticizer, then 80 ppm of different nanoparticles were added with stirring for 30 min. The solution was autoclaved (121 °C/15 min at 15 psi). Then casted onto glass petri dishes 25 × 20 cm in sterilized condition and allowed to dry overnight (18 h) in a laminar air flow at 25 °C and kept under cold storage until used. In Fig. 1a. HPMC control film without nanoparticles, Fig. 1b. HPMC film reinforced with silver Nanoparticles concentration at 80 ppm and Fig. 1c. HPMC film reinforced with titanium oxide nanoparticles concentration at 80 ppm.

Characteristic optical properties of Ag nanoparticles were recorded using PerkinElmer Lambda 35 UV–vis spectrophotometer. Spectra were recorded using 1 cm3 quartz cell. Emission spectrum (220 nm) of the solution was recorded by using spectrofluorometer from JASCO. Size, shape and particle size distributions were determined using a JEOL JEM-2011 transmission electron microscope operated at an accelerating voltage of 200 kV. Images were recorded using a Gatan DualVision 600t CCD camera attached to the microscope and were analyzed using Gatan Digital Micrograph Version 3.11.1. The TEM was calibrated for diffraction and imaging mode using standard samples. The resolution of the system was calibrated with manganese (Mn)27. Samples were prepared for TEM analysis by placing a drop of the solution on a carbon coated copper grid and drying in air. The energy dispersive X-ray analysis was undertaken with a Princeton Gamma Tech Prism 1G system with a 10 mm2 silicon detector attached to the TEM and the peaks were analysed with Imix 10.594 software27.

The X-ray diffraction (XRD) of nanoparticles were measured using X-ray diffractometer (Rigaku D/Max-B, Tokyo, Japan) according to Akbari et al28. The samples were put onto glass slide and the spectra were recorded using Cu radiation (wavelength of 0.1541 nm) and a nickel monochromator filtering wave at 40 kV and 30 mA. The average crystallite size of (TiO2-NPs) was estimated using Scherer's equation:

where D is the crystallite size, λ is the X-ray wavelength, β is the full width at have maximum of the peak and θ is the central angle of the diffraction peak.

Antibacterial activities of nanoparticles against food-borne pathogens was done by disk diffusion method on tryptic soy agar media (TSA) according to Salari et al29. The inoculum (100 μl) was adjusted nanoparticles employed in this study (20, 40 and 80 ppm), were measured after incubation at 37 °C for 24–48 h. the zones of bacterial growth inhibition were measured in mm unit.

Thicknesses of films were measured with a digital micrometer (Mitutoyo Manufacturing Co. Ltd., Japan, sensitivity ± 0.001 mm at 5 random positions on the film, following WVP and preceding tensile tests. WVP and mechanical properties were calculated based on average thickness19.

The TS, EAB, and EM of composite edible film were determined according to Hazirah et al30. An Instron Universal Testing Instrument (Model 1011) was used to determine film TS and %E. Testing film specimens were rectangular strips 38 mm long and 5.79 mm wide as suggested in ASTM D683M31. A strain rate of 50 mm/min was used. All film strips were equilibrated for one week to 52 ± 2% RH in a cabinet using saturated magnesium nitrate solution at room temperature (25 ± 1 C). At least four replicates of each MC film were tested. All three tests were performed in edible composite films31. Values for TS, EAB, and EM were calculated using:

where Fmax is the max load (N) needed to pull the sample apart and A is the cross sectional area m2 of the film sample.

where lmax is the film elongation (mm) at that moment of rupture and lo is the initial grip length (mm) of the sample.

where stress is load (N) divided by area (mm2) and strain is change in length (mm) divided by original length (mm).

WVP of films was determined gravimetrically at 25 ± 1 °C using a modified ASTM E96-8031 procedure. The test film was sealed to a glass dish containing anhydrous calcium chloride (Merck, Darmstadt, Germany), 0% RH, and the dish was placed in a desiccator maintained at 52 ± 2% RH with saturated magnesium nitrate (Merck, Darmstadt, Germany). The water vapor transferred through the film and absorbed by the desiccant was determined by measuring the weight gain. WVP was calculated from the following equation:

where WVP is in g/msPa, x is the film thickness (m), A is area of the exposed film (m2), DP is the water vapor pressure differential across the film (Pa), and C is the slope of the weight gain of the dish, to the nearest 0.0001 g, versus time. Generally, ten weighing were taken over a 7–10 h period. Slopes were calculated by linear regression and correlation coefficient (r2) for all reported data were 0.99 or greater. At least three replicates of each film type were tested for WVP.

Figure 2 shows Transparency of the films reinforced with nano-materials was determined by LS108 Spectrum Transmission Meter PL transmission meter, BL transmission meter, Light Transmittance Meter according to Hazirah et al30. It has following feature and Parameter:

PL transmission meter, BL transmission meter, Light Transmittance Meter, Three function in ONE device.

Self-calibration and auto-calibration, NO need any manual adjustments.

Simple operation, putting the testing sample in the testing position, PL, BL and VL transmission values of the sample will simultaneously display.

Size: 200 mm*180 mm*106 mm (L*W*H)

Size of Testing sample: > ¢3 mm

Accuracy: ± 2% (Colorless and transparent material)

Purple light Peak wavelength: 395 nm

Blue light Peak wavelength: 460 nm

Visible light Peak wavelength: 550 nm

Power supply: 5 V DC Adapter.

The properties of nano-materials that used in making packaging films such as silver (AgNPs) and titanium oxide (TiO2NPs) were studied. The properties of the films such as tensile strength (TS), elongation (E), Young`s elastic modulus (EM), water vapor permeability (WVP), transparency and antibacterial properties of bio-composite film were studied for the edible films reinforced with AgNPs and TiO2 -NPs.

Figure 3 shows that the spherical particles sizes were of 10 ± 2 nm diameter. TEM analysis was carried out on 100 times dilution of colloidal suspension only few particles were observed in the small section of high-resolution image. Utilization of microwave irradiation treatment showing good results not only due to faster heating but it gives uniformly distributed monodispersed particles. Colour of the solution was changed by the formation of silver nanoparticles. The characteristic surface plasmon band at 416 nm that is slightly higher was shown the visible spectrum of silver nanoparticles (Fig. 4). These results agreed with those obtained by Pal et al23,27. Silver nanoparticles had refractive index of the surrounding medium because of its slightly red shift on surface plasmon.

Shows the TEM of AgNPs a different scales (A) 100 nm, (B) 20 nm.

UV–vis and fluorescence spectroscopy of silver nanopartic.

TiO2-NPs were measured by XRD to determine the crystallite size and the purity of nanoparticles. The crystallinity size of nanoparticles was confirmed by XRD analysis as shown in Fig. 5. The XRD spectrum of dry nanoparticles were high purity, clear and broad peaks. The XRD pattern fits well with a wurtzite structure and the average crystal (diameter). Therefore, the results XRD characterization allow to conclude the nanoparticles size have a radius of around 50 ± 5 nm. These results are accordance with obtained by Aboud et al32.

XRD pattern of titanium oxide nanoparticles (TiO2-NPs).

Table 2 shows the antibacterial activities of inorganic nanoparticles i.e. Silver nanoparticles (AgNPs) and Titanium oxide nanoparticles (TiO2-NPs) against four food-borne pathogens: Bacillus cereus, Salmonella Typhimurium, E.coli and Staphylococcus aureus were evaluated results conducted that Ag-Nps (~ 10 nm) and TiO2-NPs (~ 50 nm) at 80 ppm were effective against food-borne pathogens i.e. B. cereus, S. Typhimurium, E. coli 0157:H7 and S. aureus, than 20 and 40 ppm respectively. These result with partially agreement those result indicated by Khezerlou et al33 and Ejaz et al34. Moreover, AgNPs at 80 ppm were more effective against B.Cereus and E. Coli these results agreement with data those reported by Nanda and Saravanan35. As well, TiO2-NPs at 80 ppm were more active against B.cereus and S. Typhimurium these results were similar to the results those obtained by Martinez-Gutierrez et al36. AgNPs and TiO2- NPs incorporated composite films demonstrated strong antibacterial activity against both the Gram-positive and Gram-negative food borne pathogenic bacteria.

Figure 6 shows the antibacterial activities of silver nanoparticles (Ag-NPs) and titanium oxide nanoparticles (TiO2-NPs) at different concentrations 20, 40 and 80 ppm against S.Typhimurium. The results were at a concentration of 80 ppm for (Ag-NPs) and (Tio2-NPs) more value than 20 and 40 ppm, the inhibition zone diameter was 8 and 10 mm, respectively, in Fig. 7 shows that the antibacterial activities of silver nanoparticles (Ag-NPs) and titanium oxide nanoparticles (TiO2 -NPs) at different concentration 20, 40 and 80 ppm against E. coli. The results were at a concentration of 80 ppm for (Ag-NPs) and (Tio2 -NPs) more value than 20 and 40 ppm, the inhibition zone diameter was 10 and 9 mm, respectively, in Fig. 8 shows the antibacterial activities of silver nanoparticles (Ag-NPs) and titanium oxide nanoparticles (TiO2-NPs) at different concentrations 20, 40 and 80 ppm against S.aureus. The results were at a concentration of 80 ppm for (Ag-NPs) and (TiO2 -NPs) more value than 20 and 40 ppm, the inhibition zone diameter was 8 and 8 mm, respectively, and in Fig. 9 shows the antibacterial activities of silver nanoparticles (Ag-NPs) and titanium oxide nanoparticles (TiO2-NPs) agent at concentrations 20, 40 and 80 ppm against B.cereus. The results were at a concentration of 80 ppm for (Ag-NPs) and (TiO2-NPs) more value than 20 and 40 ppm, the inhibition zone diameter was 9 and 11 mm, respectively.

Antibacterial activities of nanoparticles at different concentrations against S. Typhimurium.

Antibacterial activities of nanoparticles at different concentrations against E. coli.

Antibacterial activities of nanoparticles at different concentrations against S. aureus.

Antibacterial activities of nanoparticles at different concentrations against B. cereus.

The average of bio-composite films thickness was tested (HMPC, HMPC reinforced with AgNPs, and HMPC reinforced with TiO2NPs). As shown in Table 3, the results values of control film (HMPC), HMPC-AgNPs, and HMPC-TiO2NPs were 0.30, 0.19, and 0.12 µm, respectively.

The mechanical properties such as tensile strength, elongation, and Young`s elastic modulus were evaluated. As shown in Table 4 the tensile values of HPMC film reinforced with Ag NPs and TiO2-NPs were higher than that of tensile strength of HPMC films without nanoparticle (control), the results values were 39.24, 143.87and 157.92 MPa, respectively, for HMPC, HMPC reinforced with AgNPs, and HMPC reinforced with TiO2NPs. On the other hands, elongation was tested, the results obtained that, the HPMC film reinforced with Ag NPs and TiO2-NPs have higher value of elongation compared to than HPMC films without nanoparticle (control), the results values were 2, 35 and 42%, respectively, for HMPC, HMPC reinforced with AgNPs, and HMPC reinforced with TiO2NPs. In addition to, Young`s elastic modulus was evaluated, the results show that, HPMC film reinforced with Ag NPs and TiO2-NPs have lower values compared to than HPMC films without nanoparticle (control). The elongation values were 19.62, 4.11 and 3.76 MPa, respectively. That is due to (a) the nanoparticles’ ability to filling pore between HPMC film structures. (b) The water evaporates permeability during film formation (c) Hence, the increased surface area reinforces the (d) film thickness and biodegradable. These results are in agreement with those obtained by Martinez-Gutierrez et al36, Jiménez et al37, Silva-Weiss et al38, Ahmadi et al39, Osorio et al40 and Sievens-Figueroa et al41.

The mechanical properties such as tensile, elongation, and Young`s elastic modulus were evaluated by Using a texture analyze. In Fig. 10 shows Texture Curve of HPMC film (Control), Fig. 11 a texture analyze shows Texture Curve of HPMC- AgNPs, and Fig. 12 a texture analyze shows Texture Curve of HPMC- TiO2 NPs.

Texture Curve of HPMC film (Control).

Texture Curve of HPMC film reinforced with AgNPs.

Texture Curve of HPMC film reinforced with TiO2-NPs.

Figures 13, 14 and 15 show the relationship between the weight gain and time to calculate the slope (C) by linear regression (Y) and correlation coefficient (r2) which is used to determine of WVP transferred through the film was determined by measuring the weight gain. As shown in Table 5, the slope of bio-composite films which is used to determine of water permeability of bio-composite films reinforced with nanoparticles.

Graph of HMPC film reinforced with Ag NPs.

Graph of HMPC film reinforced with TiO2 NPs.

Table 6 shows the average of weight gain with time to determine of WVP of bio-composite films. The WVP results showed that, HPMC film reinforced with Ag NPs and TiO2-NPs were less value than that of HPMC films without nanoparticle (control), the results values were 0.5076 × 10–3 and 0.4596 × 10–3, and 0.4504 × 10–3 (g/msPa), respectively. These data revert to (a) film thickness. (b) The ability of nanoparticles to fill the pores between the HPMC films structure. (c) HPMC diffusion with different nanoparticles and form homogenized structure37. The value of the film thickness (x) of HMPC control was 0.164 µm. The values of thickness of edible films reinforced with AgNPs and TiO2NPs were 0. 1855 and 0.1455 µm, respectively. These results are in agreement with those obtained by Jiménez et al37, Silva-Weiss et al38, Ahmadi et al39, Osorio et al40 and Sievens-Figueroa et al41.

Table 7 shows the transparency of the bio-composite film based on HPMC film reinforced with nanoparticle of Ag NPs and TiO2-NPs compared to HPMC only. It could be seen that the visible light peak (VL) at different wavelengths 395, 430 and 550 nm ranged from 45 to 63% for HPMC film reinforced with Ag NPs and TiO2-NPs nanoparticle films, which it ranged from 58 to 73% for HPMC control. That is due to the difference in films reinforced with nanoparticles color42.

The bio-composite film based on Hydroxypropyl methylcellulose (HPMC) was prepared with concentrations of AgNPs and TiO2- NPs by casting method. The results have shown that some properties of the bio-composite were affected by AgNPs and TiO2- NPs content. AgNPs and TiO2- NPs caused an improvement in the WVP of the bio-composites. Transparency in control film was more value than HMPC film reinforced different nanoparticles samples. The mechanical resistance of the film increased after the formation of composite with AgNPs and TiO2 NPs. However, addition of nanoparticles resulted in increased values of elongation at break. Bio-composite films reinforced with AgNPs and TiO2-NPs incorporated demonstrated strong antibacterial activity against both the Gram-positive and Gram-negative food borne pathogenic bacteria. The added AgNPs and TiO2- NPs to HMPC film, can be used as novel active food packaging materials to prolong the shelf-life of food during storage. However, further studies are needed to determine the potential toxicity of nano-materials released from the biopolymer matrix and their migration to food.

Shuihong Zhu, Sen Wang, … Youhui Lin

Minkyung Lee, Hojung Kwak, … Dongyeop X. Oh

Junqi Yi, Guijin Zou, … Xiaodong Chen

The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.

Cross sectional area of the film sample

Slope of the weight gain of the dish

Max load needed to pull the sample apart

Film elongation at that moment of rupture and

Initial grip length of the sample

Water vapor pressure differential across the film

Full width at have maximum of the peak

Central angle of the diffraction peak

Rai, M., Yadav, A. & Gade, A. Silver nanoparticles as a new generation of Antimicrobials. Biotechnol. Adv. 27(1), 76–83 (2009).

Article  CAS  PubMed  Google Scholar 

Qureshi, M. A. et al. Application of nanotechnology in food and dairy processing: An Overview. Pak. J. Food Sci. 22(1), 23–31 (2012).

Ranjan, S., Dasgupta, N. & Ramalingam, C. Nanomaterials in food and agriculture: An overview on their safety concerns and regulatory issues. Crit. Rev. Food Sci. nutr. 58(2), 297–317 (2018).

Choi, W. S., Singh, S. & Lee, Y. S. Characterization of edible film containing essential oils in hydroxypropyl methylcellulose and its effect on quality attributes of ‘Formosa’plum (Prunus salicina L.). LWT-Food Sci. Technol. 70, 213–222 (2016).

Moghimi, R., Aliahmadi, A. & Rafati, H. Antibacterial hydroxypropyl methyl cellulose edible films containing nanoemulsions of Thymus daenensis essential oil for food packaging. Carbohydr. Polym. 175, 241–248 (2017).

Article  CAS  PubMed  Google Scholar 

Sánchez-González, L., Vargas, M., González-Martínez, C., Chiralt, A. & Cháfer, M. Characterization of edible films based on hydroxylpropyl methylcellulose and tea tree essential oil. Food Hydrocoll. 23(8), 2102–2109 (2009).

Byun, Y., Ward, A. & Whiteside, S. Formation and characterization of shellac-hydroxypropyl methylcellulose composite films. Food Hydrocoll. 27(2), 364–370 (2012).

Klangmuang, P. & Sothornvit, R. Barrier properties, mechanical properties and antimicrobial activity of hydroxypropyl methylcellulose-based nanocomposite films incorporated with Thai essential oils. Food Hydrocoll. 61, 609–616 (2016).

Kumar, R. & Münstedt, H. Silver ion release from antimicrobial polyamide/silver composites. Biomaterials 26(14), 2081–2088 (2005).

Article  CAS  PubMed  Google Scholar 

Duncan, T. V. Applications of nanotechnology in food packaging and food safety: Barrier materials, antimicrobials and sensors. J. Colloid Int. Sci. 363(1), 1–24 (2011).

Article  ADS  CAS  Google Scholar 

Cavaliere, E. et al. Highly bactericidal Ag nanoparticle films obtained by cluster beam deposition. Nanomed. Nanotechnol. Biol. Med. 11(6), 1417–1423 (2015).

Morones, J. R. et al. The bactericidal effect of silver nanoparticles. Nanotechnol. 16(10), 2346 (2005).

Article  ADS  CAS  Google Scholar 

Emamifar, A., Kadivar, M., Shahedi, M. & Soleimanian-Zad, S. Effect of nanocomposite packaging containing Ag and ZnO on inactivation of Lactobacillus plantarum in orange juice. Food Cont. 22, 408–413 (2011).

Naicker, P. K., Cummings, P. T., Zhang, H. & Banfield, J. F. Characterization of titanium dioxide nanoparticles using molecular dynamics simulations. J. Phy. Chem. 109, 15243–15249 (2005).

Liang, P., Ding, Q. & Liu, Y. Speciation of chromium by selective separation and preconcentration of Cr (III) on an immobilized nanometer titanium dioxide microcolumn. J. Sep. Sci. 29(2), 242–247 (2006).

Article  CAS  PubMed  Google Scholar 

Macwan, D. P., Dave, P. N. & Chaturvedi, S. A review on nano-TiO 2 sol–gel type syntheses and its applications. J. Mater. Sci. 46(11), 3669–3686 (2011).

Article  ADS  CAS  Google Scholar 

Shi, H., Liu, F., Yang, L. & Han, E. Characterization of protective performance of epoxy reinforced with nanometer-sized TiO2 and SiO2. Progr. Org. Coat. 62(4), 359–368 (2008).

Kubacka, A. et al. Understanding the antimicrobial mechanism of TiO2-based nanocomposite films in a pathogenic bacterium. Sci. Rep. 4(1), 1–9 (2014).

Turhan, K. N. & Şahbaz, F. Water vapor permeability, tensile properties and solubility of methylcellulose-based edible films. J. Food Eng. 61(3), 459–466 (2004).

Hussain, M. A., Elkhishin, M. & Sheng, Y. Food product innovation and food safety: Two vital elements of the global food security. J. Adv. Food Technol. Nut. Sci. 1, 47–50 (2015).

CDC. Center for Disease Control. Surveillance for foodborne disease outbreaks United States: Annual Report., 1–24 Retrieved from https://www.cdc.gov/foodsafety/pdfs/2015foodborneoutbreaks_508pdf, (2017).

World Bank. Global data and statistics, research and publications, and topics in poverty and development. https://www.worldbank.Org/en/news/pressrelease23/10/2018food-borne-illnessess-cost-us-110billionperyearinlowandmiddle-incomecountries. 1–5 (2018).

Pal, A., Shah, S. & Devi, S. Synthesis of Au, Ag and Au–Ag alloy nanoparticles in aqueous polymer solution. Colloids Surf. A Physicochem. Eng. Aspects 302, 51–57 (2007).

Fu-Ken, L. et al. Microwave-assisted synthesis of silver nanoparticles using ethanol as a reducing agent. Mater. Chem. Phys. 114, 530–532 (2005).

Salah, N. et al. High-energy ball milling technique for ZnO nanoparticles as antibacterial material. Int. J. Nanomed. 6, 863 (2011).

De Moura, M. R. et al. Improved barrier and mechanical properties of novel hydroxypropyl methylcellulose edible films with chitosan/tripolyphosphate nanoparticles. J. Food Eng. 92(4), 448–453 (2009).

Pal, A., Shah, S. & Devi, S. Microwave-assisted synthesis of silver nanoparticles using ethanol as a reducing agent. Mater. Chem. Phys. 114, 530–532 (2009).

Akbari, B., Tavandashti, M. P. & Zandrahimi, M. Particle size characterization of nanoparticles: A practical approach. Iran. J. Mater. Sci. Eng. 8(2), 48–56 (2011).

Salari, M., Khiabani, M. S., Mokarram, R. R., Ghanbarzadeh, B. & Kafil, H. S. Development and evaluation of chitosan based active nanocomposite films containing bacterial cellulose nanocrystals and silver nanoparticles. Food Hydrocoll. 84, 414–423 (2018).

Hazirah, M. N., Isa, M. I. N. & Sarbon, N. M. Effect of xanthan gum on the physical and mechanical properties of gelatin-carboxymethyl cellulose film blends. Food Pack. Shelf Life 9, 55–63 (2016).

ASTM. Standard test methods for water vapor transmission of materials. E 96–80, Annual Book of ASTM Standards, Philadelphia, PA, pp. 761–770 (1983).

Aboud, A. A. et al. CO2 responses based on pure and doped CeO2 nano-pellets. J. Mater. Res. Technol. 7(1), 14–20 (2018).

Khezerlou, A., Alizadeh-Sanib, M., Azizi-Lalabadib, M. & Ehsani, A. Nanoparticles and their antimicrobial properties against pathogens including bacteria, fungi, parasites and viruses. J. Microb. Pathog. 123(2), 505–526 (2018).

Ejaz, M., Arfat, Y. A., Mulla, M. & Ahmed, J. Zinc oxide nanorods/clove essential oil incorporated type B gelatin composite films and its applicability for shrimp packaging. Food Pack. Shelf Life 15, 113–121 (2018).

Nanda, A. & Saravanan, M. Biosynthesis of silver nanoparticles from Staphylococcus aureus and its antimicrobial activity against MRSA and MRSE. Nanomed. Nanotechnol. Biol. Med. 5(4), 452–456 (2009).

Martinez-Gutierrez, F. et al. Synthesis, characterization, and evaluation of antimicrobial and cytotoxic effect of silver and titanium nanoparticles. Nanomed. Nanotechnol. Biol. Med. 6(5), 681–688 (2010).

Jiménez, A., Fabra, M. J., Talens, P. & Chiralt, A. Effect of lipid self-association on the microstructure and physical properties of hydroxypropyl-methylcellulose edible films containing fatty acids. J. Carbohydr. Poly. 82(3), 585–593 (2010).

Silva-Weiss, A. A., Ihi, M. P., Sobral, P. J. A., Gómez-Guillén, M. C. & Bifani, V. Natural additives in bioactive edible films and coatings: Functionality and applications in foods. J. Food Eng. 5, 200–216 (2013).

Ahmadi , R. , Kalbasi-Ashtari , A. , Oromiehie , A. , Yarmand , MS & Jahandideh , F. Development and characterization of a novel biodegradable edible film obtained from psyllium seed ( Plantago ovata Forsk ).J. Food Eng.109(4), 745–751 (2012).

Osorio, F. A., Molina, P., Matiacevich, S., Enrione, J. & Skurtys, O. Characteristics of hydroxy propyl methyl cellulose (HPMC) based edible film developed for blueberry coatings. J. Procedia Food Sci. 1, 287–293 (2011).

Sievens-Figueroa, L. et al. Preparation and characterization of hydroxy propyl methyl cellulose films containing stable BCS Class II drug nanoparticles for pharmaceutical applications. Int. J. Pharm. 423(2), 496–508 (2012).

Article  CAS  PubMed  Google Scholar 

Osman, A. G., El-Desouky, A. I., Morsy, M. K., Aboud, A. A. & Mohamed, M. H. Impact of aluminum oxide and silica oxide nanocomposite on foodborne pathogens in chicken fillets. Eur. J. Nut. Food Saf. 9, 152–162 (2019).

His work is fully sponsored by the Support and Development of Scientific Research Center, Benha University. We would also like to show our gratitude to the Arab Academy for Science and Technology and Maritime Transport, Cairo, Egypt.

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). This research was supported by the Support and Development of Scientific Research Center, Benha University, Egypt. We would also like to show our gratitude to the Arab Academy for Science and Technology and Maritime Transport, Cairo, Egypt.

Agricultural and Biosystems Engineering Department, Faculty of Agriculture, Benha University, P.O. Box 13736, Moshtohor, Toukh, Kalubia, Egypt

El-Sayed Khater, Adel Bahnasawy & Basma Abu Gabal

Basic and Applied Science Department, College of Engineering and Technology, Arab Academy for Science and Technology and Maritime Transport (AASTMT), P.O. Box 2033, Cairo, Egypt

Wael Abbas & Osama Morsy

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

E-S., A.B., B.A.G., W.A. and O.M.: Investigation, Resources, Writing—Original Draft Preparation, Writing—Review and Editing.

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, and in the decision to publish the results.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Khater, ES., Bahnasawy, A., Gabal, B.A. et al. Effect of adding nano-materials on the properties of hydroxypropyl methylcellulose (HPMC) edible films. Sci Rep 13, 5063 (2023). https://doi.org/10.1038/s41598-023-32218-y

DOI: https://doi.org/10.1038/s41598-023-32218-y

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

International Journal of Theoretical Physics (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Scientific Reports (Sci Rep) ISSN 2045-2322 (online)

Effect of adding nano-materials on the properties of hydroxypropyl methylcellulose (HPMC) edible films | Scientific Reports

hydroxymethyl propyl cellulose Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.